1cr11MOV 1.4922 X20crmov11-1 Stainless Steel for Steam Turbine Blade

• Customization: Available
• After-sales Service: Support
• Type: Heat Resisting Austenitic Steel
• Model NO.: Heat Resisting Steel
• Standard: AISI, ASTM, GB, JIS, DIN, BS
• Technique: Cold Drawn, Hot Rolled, Forged, Grinding, etc.
• Application: Structural Steel Bar, Tool Steel Bar, Die Steel Bar
• Surface Treatment: Polished
• Alloy: Alloy
• Special Use: Mold Steel, Free Cutting Steel, Cold Heading Steel
• Certificate: ISO, ABS, BV, CCS, Dnv, Lr, Gl, Mill Certificate
• Quality Inspection: Ut, Chemical Composition, Physical Properties/SGS
• Length: Normally 6m, or Produce as Requirements
• Diameter: 4mm - 600mm
• Diameter Tolerance: H9, H11, H13, K9, K11, K13 etc
• Heat Treatment: Quenched, Tempered, Annealed
• Surface Require: Black, Bright. Peeled and Polished, Annealed
• Transport Package: Seaworthy Packing/Wooden Box or at Client′s Requir
• Specification: Customized
• Trademark: OEM & ODM
• Origin: China
• HS Code: 7219350000
• Production Capacity: 1000 Ton/Month

Product Description

Product Description

 

Supplying dimension

Round bar from         30mm to 600mm Diameter

Flat and square bar from  30mm to 500mm Width

8mm to 300mm Thickness

*accept special shape

Forming option

Hot rolling or hot forged

Smelting process

EAF →VD→LF→ESR Electro-Slag Remelting

Surface option

Black

Grinding

Rough turned

Peeled

Polished

Quality

UT, size and surface for each pcs

Macrostructure

Ferritic Metallographic

Grain size

Nonmetallic inclusion

Etch test of tower sample

Delivery condition and hardness

Annealed or high temperature temper

Annealed	high temperature temper	Hardness
800 to 900 Celsius, slow	700 to 770 Celsius, fast	Max 200 HBW

*Accept +QT delivery condition

Equivalent Grade

Chinese UNS	Chinese New Grade	Chinese Old Grade	EN BS DIN	EN BS DIN
S46010	14Cr11MoV	1Cr11MoV	1.4922	X20CrMoV11-1

Chemical component

C	Si	Mn	P	S	Ni	Cr	Cu	Mo	V
0.11 to 0.18	Max 0.50	Max 0.60	Max 0.030	Max 0.020	Max 0.60	10.00 to 11.50	Max 0.30	0.50 to 0.70	0.25 to 0.40

Mechanical property and heat treatment

Type	Quench temperature	Temper temperature	Specified Plastic Elongation Strength	Tensile strength	Elongation	Reduction	Impact	Hardness
1	1000 to 1050 Celsius, air, oil	700 to 750 Celsius, air	Min 490 Mpa	Min 685 Mpa	Min 16 %	Min 56%	Min 27 KJ	212 to 262 HBW
2	1000 to 1030 Celsius, oil	660 to 700 Celsius, air	Min 590 Mpa	Min 735 Mpa	Min 15 %	Min 50%	Min 27 KJ	229 to 277 HBW

 