High Strength High Speed Tool Steel for Cutters T1 1.3355 Skh2 W18cr4V

Product Description

Product Description

ASTM T1 1.3355 HS18-0-1 SKH2 High Speed Tool Steel

1. T1 steel introduction

    T1 tool steel is one of the original tungsten high speed steels, although all tungsten steel grades are used to a limited extent because of the cost and questionable availability of tungsten. Of the T group steels, the general purpose T1 tool steels and the high-vanadium-cobalt T15 are most commonly used.

 

2. T1 Steel equivalent

Country	USA	German	Japan
Standard	ASTM A600	DIN EN ISO 4957	JIS G4403
Grade	T1	1.3355/HS18-0-1	SKH2

 
3. T1 steel chemical composition

Grade	C	Si	Mn	P	S	Cr	Mo	V	W	Co
T1	0.62-0.8	0.2-0.4	0.1-0.4	0.03	0.03	3.75-4.5	/	0.9-1.3	17.25-18.75	/
1.3355	0.73-0.85	0.65	0.4	0.03	0.03	3.6-4.5	/	1.0-1.2	17.2-18.7	/
SKH2	0.73-0.83	0.45	0.4	0.03	0.03	3.8-4.5	/	1.0-1.2	17.2-18.7	/

 
4. T1 steel mechanical properties  

    The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.

 

5. T1 steel overviews

Size	Round	Dia 2-300mm
	Plate/Flat/Block	Thickness 2mm-20mm
		Width 10mm-100mm
Heat treatment	Normalized ; Annealed ; Quenched ; Tempered
Surface condition	Black; Peeled; Polished; Machined; Grinded; Turned; Milled
Delivery condition	Forged; Hot rolled; Cold drawn
Test	Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc.
Payment terms	T/T;L/C;/Money gram/ Paypal
Trade terms	FOB; CIF; C&F; etc..
Delivery time	30-45 days
Application	T1 are used for Broaches, Drills, Hobs, Knurling Tools, Lathe Tools, Milling Cutters, Nut Piercers, Planer Tools, Reamers, Shaving Tools, Taps, Thread Cutting Tools.

 

 

6. T1 Steel Heat Treatment and Properties

Treatment	Temperature Range	Cooling/Quenching	Notes
Forging	1700-2100° F	Slow.	Cool slowly in dry sand or in other insulating media.
Annealing	1600-1650° F	Cool slowly at a rate of 35° F per hour to 1000° F.	For best results, insulating media is desirable. Hold at temperature for 2 hours.
Stress Relieving	1100-1300° F	Cool slowly	Stress relieve after rough machining
Preheating	1500-1550° F		Preheat time in furnace is ¾ Hr. per inch of thickness. Heating up to temperature as slow as possible.
Hardening	2325-2375° F (furnace)	Quench in air or warm oil. To minimize quenching strains, quench in salt at 1000° F	For maximum wear resistance, harden at 2375° F. For maximum toughness and high hardness, harden at 2275° F.
	2275-2350° F (salt bath)
Tempering	1022 ° F-1058 ° F	Temper T1 high-speed steel immediately after quenching. Hold for at least two hours	Double tempering is recommended. The usual tempering time is 2+2 hours. Recommended temperature is 1000-1075° F for cutting tools. 1100-1200° F for shock tools

 

7. Delivery condition

    For hot rolled bar, usually the delivery condition is hot rolled, annealed, Black surface.
    For cold drawn plate, usually the delivery condition is cold drawn, annealed, milled surface
    For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.
 

 

Main Products

 

	AISI	DIN	JIS	Stock	Application
Hot Work Tool Steel	H11	1.2343	SKD6	√	Die Casting Dies,Extrusion Dies, Hammer Dies, Ram Dies, Forging Dies etc.
	H13	1.2344	SKD61	√
	H10	1.2365	SKD7
	--	1.2367	--
	L6	1.2714 / 1.2713	SKT4	√
	H12	1.2606	SKD62
	H21	1.2581	SKD5	√
Cold Work Tool Steel	D3	1.2080	SKD1	√	Cutting Tools, Punching Tools, Shear Bladers, Reamers, Thread Rolling Dies, Calipers, Sockets etc.
	--	1.2601	~SKD11	√
	D2	1.2379	~SKD11	√
	--	1.2379 MOD	DC53 (Daido)	√
	D6	1.2436	--
	O1	1.2510	SKS3	√
	O2	1.2842	--
	A2	1.2363	SKD12
	S1	1.2550	--
	S7	1.2357	--
	--	1.2767	SKT6
	L2	1.2210	--
Plastic Mould Steel	P20	1.2311	--	√	Mold Base, Core & Cavity, Bumper Mold etc.
	P20+Ni	1.2738	--	√
	P20+S	1.2312	--	√
	--	1.2316	--
	420	1.2083	SUS420J2	√
	--	--	NAK80 (Daido)	√
Alloy Steel	4120	25CrMo4 / 1.7218	SCM420		Shafts, Gears, Drillers, Chains, Bolts, Nuts, Pins, Suds, Keys, Bites, Crankshafts, Connecting Rods, Came, Couplings etc.
	4135	34CrMo4 / 1.7220	SCM435
	4130	34CrMo4 / 1.7220	SCM430	√
	4140	42CrMo4 / 42CrMoS4 / 1.7225	SCM440	√
	4142	41CrMo4 / 1.7223	SCM440
	4145H	--	--
	4330V	--	--
	4340	34CrNiMo6 / 1.6582	SNCM439
	5115	16MnCr5 / 16MnCrS5 / 1.7131
	5120	20MnCr5 / 20MnCrS5 / 1.7147	SMnC420H
	5140	41Cr4 / 41CrS4 / 1.7035	SCr440	√
	8620	21NiCrMo2 / 1.6523	SNCM220
	8640	40NiCrMo2-2 / 1.6546	SNCM240
	--	18CrNiMo7-6 / 17CrNiMo6 / 1.6587	--
	9840	36CrNiMo4 / 1.6511	--
	E71400	41CrAlMo7-10 / 1.8509	SACM1
	--	34CrAlNi7 / 1.8550	--
Bearing Steel	E52100	100Cr6 / 1.3505	SUJ2	√	Bearing, Shafts etc.
	--	100CrMn6 / 1.3520	--
	--	100CrMo7-3 / 1.3536	--
Spring Steel	5155	55Cr3 / 1.7176	SUP9		Springs
	6150	51CrV4 / 1.8159	SUP10
	9261	60CrSi7 / 1.7108	--
Carbon Steel	1010	CK10 / C10E / 1.1121	S10C		Shafts, Chains, Bolts, Nuts, Pins, Suds, Keys, Bites, Came, Couplings etc.
	1020	C22 / 1.0402	S20C	√
	1040	CK40 / C40E / 1.1186	S40C	√
	1045	CK45 / C45E / 1.1191	S45C	√
	1050	CK50 / C50E / 1.1206	S50C	√
	1055	CK55 / C55E / 1.1203	S55C
	1064	CK60 / C60E / 1.1221	S58C
High Speed Tool Steel	M2	1.3343	SKH51	√	Reamer, End-mill, Hob, Cutter, Bite, Drill, Punch, Tap, Brooch etc.
	M7	1.3348	--
	M42	1.3247	SKH59	√
	M35	1.3243	SKH55	√
	T1	1.3355	SKH2
	T15	1.3202	--
	T42	1.3207	SKH57